产物与市场
Autolad1
特色
● 无铅兼容FR-4.0板材
● 低的Z轴热收缩系数
● 良好的耐CAF及TCT机能
● 较低的吸水率
利用范畴
● 汽车电子公用资料，合用于车内电路接线盒、发念头和车身的电子节制单位- 产物机能
- 产物证书
- 资料下载
| Items | Method | Condition | Unit | Typical Value |
|---|---|---|---|---|
| Tg | 2.4.24.4 | DMA | ℃ | 160 |
| 2.4.25D |
DSC |
155 | ||
| Td | 2.4.24.6 | 5% wt. loss | ℃ | 348 |
|
T288 |
2.4.24.1 | TMA | min | 20 |
| T260 |
2.4.24.1 |
TMA |
min |
60 |
|
Thermal Stress |
2.4.13.1 |
288℃, solder dip |
- |
>100s No Delamination |
| CTE (Z-axis) | 2.4.24 | Before Tg | ppm/℃ | 37 |
| After Tg | ppm/℃ | 230 | ||
| 50-260℃ | % | 2.8 | ||
| Dissipation Constant (1GHz) | 2.5.5.9 | C-24/23/50 | - | 4.6 |
|
Dissipation Factor (1GHz) |
2.5.5.9 |
C-24/23/50 |
- | 0.011 |
| Volume Resistivity | 2.5.17.1 | C-96/35/90 | MΩ.cm | 1.5×108 |
|
Surface Resistivity |
2.5.17.1 |
C-96/35/90 | MΩ | 3.5×107 |
| Arc Resistance | 2.5.1 | D-48/50+D-0.5/23 | s | 150 |
| Dielectric Breakdown | 2.5.6 | D-48/50+D-0.5/23 | kV | 45+kV NB |
| Peel Strength (1Oz) | 2.4.8 | 288℃/10s | N/mm | 1.3 |
| Flexural Strength (LW/CW) | 2.4.4 | A | MPa | 530/440 |
| Water Absorption | 2.6.2.1 | E-1/105+D-24/23 | % | 0.09 |
|
Flammability |
UL94 |
C-48/23/50 |
Rating |
V-0 |
| CTI | IEC60112 | A | Rating | PLC3 |
Remarks:
1. All the typical value is based on the 1.6mm specimen. Test method is according to IPC-TM-650.2. All the typical values listed above are for your reference only and not intended fors pecification. Please contact Shengyi Technology Co., Ltd. for detailed information. All rights from this data sheet are reserved by Shengyi Technology Co., Ltd.
Explanation: C=Humidity conditioning, D=Immersion conditioning in distilled water, E=Temperature conditioning
The first digit following the letter indicates the duration of preconditioning in hours, the second digit the preconditioning temperature in ℃ and the third digit the relative humidity.